904L Stainless Steel Coil Strip

Grade 904L stainless steel is a non-stabilized austenitic stainless steel with low carbon content. This high alloy stainless steel is added with copper to improve its resistance to strong reducing acids, such as sulphuric acid. The steel is also resistant to stress corrosion cracking and crevice corrosion. Grade 904L is non-magnetic, and offers excellent formability, toughness and weldability. The coil and strip supplied by wenzhou taixin steel co.,ltd will help you enjoy good quality and expand market.

Availability:



Inquire

Standard: ASTM, AISI, JIS, GB ,SUS
Thickness: 0.2mm~150mm
Width: 40-2000mm or as your requirement
Length: 2000-11000mm or as your requirement
Technique: hot rolled: 3~150mm thickness
cold rolled: 0.2~6mm thickness
Surface: 2B, BA, No.4,HL,No.1 ,etc

2B	The surface brightness and flatness of 2B is better than 2D then theough a special surface treatment to improve its mechanical properties,2B could nearly Satisfy comprehensive uses
No.3	Polished with abrasive belt of git#100#200#,have better brightness with discontinuous coarse stria used as inner and external omaments for building, electrical appliances and kitchen utensils etc.
No.4	Polished with abrasive belt of grit#150#180,have better brightness with discontinuous coarse stria, but thinner than NO.3, are used as bathtub buildings inner and extemal omaments electrical appliances kitchen utensils and food processing
BA	Cold rolled, bright annealed and skin-passed, the product have excellent brightness and food reflexivity like mirrorm kitchen apparatus, omament etc.
8K	The product have excellent brightness and prefer reflexivity can be the mirror.
HL	Polished with abrasive belt of trit#150#320 on the NO.4 finish and has continuous streaks, mainly used as buildings omaments elevators, door of building, frontal plate etc.

904L Stainless Steel Coil Strip

FEEDBACK FROM CONTACT WITH US

Grade		C	Mn	Si	P	S	Cr	Mo	Ni	Cu
904L	min. max.	- 0.02	- 2	- 1	- 0.045	- 0.035	19 23	4 5	23 28	1 2

Grade	Tensile Strength (MPa) min	Yield Strength 0.2% Proof (MPa) min	Elongation (% in 50mm) min	Hardness
				Rockwell B (HR B)	Brinell (HB)
904L	490	220	36	70-90 typical	150

Grade	Density (kg/m3)	Elastic Modulus (GPa)	Mean Co-eff of Thermal Expansion (µm/m/°C)			Thermal Conductivity (W/m.K)		Specific Heat 0-100°C (J/kg.K)	Elec Resistivity (nΩ.m)
			0-100°C	0-315°C	0-538°C	At 20°C	At 500°C
904L	7900	190	15	-	-	11.5	-	500	952

Grade		C	Mn	Si	P	S	Cr	Mo	Ni	Cu
904L	min. max.	- 0.02	- 2	- 1	- 0.045	- 0.035	19 23	4 5	23 28	1 2

Grade	Tensile Strength (MPa) min	Yield Strength 0.2% Proof (MPa) min	Elongation (% in 50mm) min	Hardness
				Rockwell B (HR B)	Brinell (HB)
904L	490	220	36	70-90 typical	150