Alloy 420 is a martensitic stainless steel of the 12% Chromium type. Due to it's Chromium content 420 will achieve high hardness. Alloy 420 is used in many different applications including surgical and dental instruments, scissors, needle valves, gears, ball bearings, magnets etc. Alloy 420 should not be used for springs or heavily stressed parts that require to be operated at sub-zero temperatures.
Grade 430, also known as type WL 1.4016 stainless steel combines good corrosion resistance with good formability and ductility. As Grade 430 has excellent resistance to nitric attack it is well suited to use in chemical applications. Grade 430 is generally used for domestic appliances, flue linings, scientific apparatus etc.
Grade 440C stainless steel is a high carbon martensitic stainless steel. With high strength, moderate corrosion resistance, and good hardness and wear resistance.
Grade 440C is capable of attaining, after heat treatment, the highest strength, hardness and wear resistance of all the stainless alloys. Its very high carbon content is responsible for these characteristics, which make 440C particularly suited to such applications as ball bearings and valve parts.
Alloy 420 is a martensitic stainless steel of the 12% Chromium type. Due to it's Chromium content 420 will achieve high hardness. Alloy 420 is used in many different applications including surgical and dental instruments, scissors, needle valves, gears, ball bearings, magnets etc. Alloy 420 should not be used for springs or heavily stressed parts that require to be operated at sub-zero temperatures.
Grade 430, also known as type WL 1.4016 stainless steel combines good corrosion resistance with good formability and ductility. As Grade 430 has excellent resistance to nitric attack it is well suited to use in chemical applications. Grade 430 is generally used for domestic appliances, flue linings, scientific apparatus etc.
Grade 440C stainless steel is a high carbon martensitic stainless steel. With high strength, moderate corrosion resistance, and good hardness and wear resistance.
Grade 440C is capable of attaining, after heat treatment, the highest strength, hardness and wear resistance of all the stainless alloys. Its very high carbon content is responsible for these characteristics, which make 440C particularly suited to such applications as ball bearings and valve parts.
Chemical Composition:
Chemical Composition Limits | |||||||
Weight% | C | P | Si | Fe | Mn | S | Cr |
Alloy 420 | 0.15 min | 0.040 max | 1.00 max | Bal | 1.00 max | 0.030 max | 12-14 |
Typical Mechanical Properties:
Material | Tensile Strength (Mpa) | Proof Stress 0.2% (MPa) | % Elongation in 2" | % Reduction of Area | Hardness Brinell |
Alloy 420 Ann | 655 | 345 | 25 | 55 | 196 |
Chemical Composition:
Chemical Composition Limits | |||||||||||
Weight% | C | Mn | Si | P | S | Cr | Ni | Mo | Cu | Al | Sn |
Alloy 430 | 0.12 max | 1.00 | 1.00 | 0.04 | 0.03 | 16-18 | 0.75 max | 0.50 | 0.50 | 0.05 | 0.05 |
Typical Mechanical Properties:
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
430 | 483 | 310 | 22 | 85 | 183 |
Chemical Composition:
440C Stainless | ||
Nickel (Ni) | 0.75% | |
Molybdenum | 0.75% | |
Copper (Cu) | 0.5% | |
Manganese | 1% max | |
Iron (Fe) | Balance | |
Carbon (C) | 0.95 – 1.2% | |
Chromium (Cr) | 16 – 18% | |
Manganese (Mn) | 1% max | |
Phosphorus (P) | 0.04% max | |
Sulphur (S) | 0.03% max | |
Silicon (Si) | 1% max |
Chemical Composition:
Chemical Composition Limits | |||||||
Weight% | C | P | Si | Fe | Mn | S | Cr |
Alloy 420 | 0.15 min | 0.040 max | 1.00 max | Bal | 1.00 max | 0.030 max | 12-14 |
Typical Mechanical Properties:
Material | Tensile Strength (Mpa) | Proof Stress 0.2% (MPa) | % Elongation in 2" | % Reduction of Area | Hardness Brinell |
Alloy 420 Ann | 655 | 345 | 25 | 55 | 196 |
Chemical Composition:
Chemical Composition Limits | |||||||||||
Weight% | C | Mn | Si | P | S | Cr | Ni | Mo | Cu | Al | Sn |
Alloy 430 | 0.12 max | 1.00 | 1.00 | 0.04 | 0.03 | 16-18 | 0.75 max | 0.50 | 0.50 | 0.05 | 0.05 |
Typical Mechanical Properties:
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
430 | 483 | 310 | 22 | 85 | 183 |
Chemical Composition:
440C Stainless | ||
Nickel (Ni) | 0.75% | |
Molybdenum | 0.75% | |
Copper (Cu) | 0.5% | |
Manganese | 1% max | |
Iron (Fe) | Balance | |
Carbon (C) | 0.95 – 1.2% | |
Chromium (Cr) | 16 – 18% | |
Manganese (Mn) | 1% max | |
Phosphorus (P) | 0.04% max | |
Sulphur (S) | 0.03% max | |
Silicon (Si) | 1% max |
The key applications of grade 420 stainless steels include:
● Shear blades
● Needle valves
● Surgical equipment
● Cutlery
The following are the applications for stainless steel grade 430:
● Dish washer linings
● Refrigerator cabinet panels
● Element supports and fasteners
● Stove trim rings and chimney liners
● Automotive trim and lashing wires
Grade 440C stainless steel is used in the following applications:
● Gage blocks
● Cutlery
● Ball bearings and races
● Molds and dies
● Knives
● Valve components
● Measuring instruments
The key applications of grade 420 stainless steels include:
● Shear blades
● Needle valves
● Surgical equipment
● Cutlery
The following are the applications for stainless steel grade 430:
● Dish washer linings
● Refrigerator cabinet panels
● Element supports and fasteners
● Stove trim rings and chimney liners
● Automotive trim and lashing wires
Grade 440C stainless steel is used in the following applications:
● Gage blocks
● Cutlery
● Ball bearings and races
● Molds and dies
● Knives
● Valve components
● Measuring instruments
The bars are wrapped with anti-rust paper and steel rings to prevent damage. Identification labels are tagged according to standard specification or customer's instructions. Special packing is available as per customer's requirement.Ply wooden box are available for special protection. Other kinds of packing can be offered if request.
The bars are wrapped with anti-rust paper and steel rings to prevent damage. Identification labels are tagged according to standard specification or customer's instructions. Special packing is available as per customer's requirement.Ply wooden box are available for special protection. Other kinds of packing can be offered if request.
Add: Maao Industry Area,Jiangbei district,Wenzhou City, Zhejiang Province,China
Tel: +86-21-80510189
+86-21-80510198
E-mail: sales@alloyss.com